Metal Surface Catalytic Alloy (Nickel Phosphorus Coating)

　　The technology of Electroless nickel phosphorus alloy is a new type of metal surface protection and reinforcement technology The principle is that under the condition of no applied current, using the action of reducing agent, by means of chemical deposition, the metal Ni+ in the plating solution is precipitated and deposited on the surface of the base material with catalytic activity, and a layer of amorphous state single-phase tissue of Ni-P alloy coating is obtained The coating does not have crystal defects such as grain boundary dislocation, and it is not easy to form electric coupling corrosion, so the coating has high corrosion resistance in acid-base salt and organic medium The unique uniformity, compactness and integrity of the coating provide a very ideal shielding protection for the base material

Related products

Performance features and technical indicators
Others

Product performance features

1. Uniform thickness of the coating: the average thickness change within ± 5%, no permeability limit, strictly maintain the geometry of the coated workpiece.

2. Strong adhesion of the coating: on the substrate surface is the compressive stress, the binding force is generally 400Mpa.

3. High hardness of the coating: surface hardness up to 550HV, good wear resistance.

4. Good temperature resistance of the coating: at 700 ℃ not Soften, no peeling, do not fall off.

5. Good compactness of the coating: low porosity, coating greater than 30μm, can be achieved without pinhole.

6. Good integrity of the coating: the elongation is 0.5%-1.5% can be fully bent without cracks.

Scope of application

The excellent properties of Ni-P alloy coating with high corrosion resistance and the successful application of this technology in petroleum processing enterprises over the years have solved the corrosion problems of such as HCL, H2S, FeCL3 and naphthenic acid encountered in production. In many systems of refinery production plants such as usual decompression device fractionation system, heavy oil catalytic cracking unit, delayed coking device, catalytic reforming device, gas fractionation device, hydrogenation device, sulfuric acid recovery device, aromatic extraction device and other systems, operating temperature in the 100℃-380℃ range, the working medium contains H2S,Sulfur and sulfide monomer, Naphthenic acid, HCL and CL-components and other corrosive media equipment, can be used Ni-P alloy coating process technology. It can effectively solve the equipment encountered by high temperature sulfur corrosion, FeCL3 corrosion, inorganic acid and organic acid and other acidic media caused by chemical corrosion, H2S caused by stress corrosion cracking, CL-formation of point corrosion and many other corrosion problems, to ensure the safe operation of equipment.

Multifunctional electroless plating Ni-P alloy technology can be widely used in oil extraction, oil processing enterprises in heat transfer equipment, coil, injection well oil pipe, control pump valve, instrumentation, absorption piston rod, rotary shaft, impeller, mixer, reaction kettle, filter, center separator, etc., can also be used in fertilizer, metallurgy, automotive, electronics, shipbuilding , Textile, food and many other industries related equipment, play an active and effective protection role.